Castables
Brand Name | Al2O3 (%) |
Fe2O3 (%) |
B.D. (gm/cc) |
CCS (kg/cm2) |
PCE (C) Min. |
Grain Size | |
---|---|---|---|---|---|---|---|
Dried at 110C/24hrs | Fired at 1400C/3hrs | ||||||
TRL Cast AH 50 | ≥ 50 | ≤ 1.50 | ≥ 2.1 | ≥ 350 | ≥ 400 | ≥ 1660 | ≤ 5 |
TRL Cast AH 60 | ≥ 60 | ≤ 1.50 | ≥2.15 | ≥ 350 | ≥ 450 | ≥ 1680 | ≤ 5 |
TRL Cast AH 90 | ≥ 88 | ≤ 1.50 | ≥ 2.70 | ≥ 550 | ≥ 550 | ≥ 1780 | ≤ 5 |
TRL Cast FH 40 | ≥ 40 | ≤ 2.5 | ≥ 1.90 | ≥ 250 | ≥ 350 | 1500 | ≤ 5 |
TRL Cast FH 45 | ≥ 45 | ≤ 4.0 | ≥ 2.10 | ≥ 250 | ≥ 350 | ≥ 1580 | ≤ 5 |
TRL Cast FH 70 | ≥ 70 | ≤ 5.0 | ≥ 2.50 | ≥ 350 | ≥ 450 | ≥ 1680 | ≤ 5 |
TRL Cast LC 45 | ≥ 45 | ≤ 1.25 | ≥ 2.30 | ≥ 700 | ≥ 1000 | ≥ 1720 | ≤ 5 |
TRL Cast LC 60 | ≥ 60 | ≤ 1.50 | ≥ 2.40 | ≥ 700 | ≥ 1000 | ≥ 1800 | ≤ 5 |
TRL Cast BG | 30-35 | ≤ 5.0 | 1.80-2.00 | 150 – 250 | ≤ 5 | ||
TRL Incast 7 | ≥ 25 | ≤ 5 | ≥ 0.85 | ≤ 5 | |||
TRL Incast 9 | ≥ 25 | ≤ 4 | ≥ 1.10 | ≤ 5 | |||
TRL Incast 11 | ≥ 35 | ≤ 4 | ≥ 1.30 | ≤ 5 |
Mortar
Brand Name | Setting | Al2O3 (%) |
Fe2O3 (%) |
Sintering Temp |
Application Temp |
PCE (SK) Min. |
Grain Size (mm) |
---|---|---|---|---|---|---|---|
TRL HGM | Ceramic | ≥ 33 | ≤ 2.50 | 1300 | 1400 | ≥ 32 | ≤ 0.5 |
TRL 45M | Ceramic | ≥ 42 | ≤ 2.00 | 1350 | 1450 | ≥ 33 | ≤ 0.5 |
TRL 50M | Ceramic | ≥ 48 | ≤ 2.00 | 1350 | 1480 | ≥ 34 | ≤ 0.5 |
TRL 60M | Ceramic | ≥ 60 | ≤ 2.00 | 1350 | 1500 | ≥ 35 | ≤ 0.5 |
TRL 70M | Ceramic | ≥ 70 | ≤ 2.00 | 1550 | ≥ 35 | ≤ 0.5 | |
TRL Mul 70M | Ceramic | ≥ 70 | ≤ 2.00 | 1580 | ≥ 35 | ≤ 0.5 | |
TRL 80M | Ceramic | ≥ 80 | ≤ 2.5 | 1600 | ≥ 36 | ≤ 0.5 | |
TRL 85M | Ceramic | ≥ 85 | ≤ 2.00 | 1600 | ≥ 36 | ≤ 0.5 | |
TRL Set 50N | Ceramic | ≥ 50 | ≤ 2.00 | 1350 | ≥ 34 | ≤ 0.5 | |
TRL Set N | Ceramic | ≥ 40 | ≤ 2.50 | 1300 | ≥ 33 | ≤ 0.5 |